Aluminum honeycomb core
Description: aluminum honeycomb core is made of multilayer foil bonded, laminated and then pull stretched into honeycomb shapes. As a family of cellular "aristocracy", aluminum honeycomb has a very good performance, high strength, high temperature resistance, corrosion resistance, is used on the aviation, aerospace, ideal material for high-speed ships, high-speed trains and so on. In the construction industry it is used preferentially on the large size wall and indoor decoration materials with the flame retardant of demanding. Our company produces aluminum honeycomb core made of high quality aluminum foil (thickness 0.03mm~0.25mm) and high strength adhesive processing, and advanced technology, strict production control, honeycomb has high bond strength and stable performance.
|
铝蜂窝芯主要规格参数
|
边长
|
孔距
|
铝箔厚度
|
公称密度Kg/M3
|
压缩稳定性(常温)
|
可展开尺寸(长×宽)
|
|
强度MPa
|
模量MPa
|
|
1.5 mm
|
2.6 mm
|
0.03 mm
|
82.9
|
4.2
|
926
|
1200×2400 mm
|
|
2 mm
|
3.4 mm
|
0.04 mm
|
82.8
|
3.1
|
713
|
1200×2400 mm
|
|
2.5 mm
|
4.3 mm
|
0.04 mm
|
66.4
|
2.7
|
561
|
1200×2400 mm
|
|
3 mm
|
5.2 mm
|
0.04 mm
|
55.3
|
1.6
|
324
|
1200×2400 mm
|
|
4 mm
|
6.9 mm
|
0.05 mm
|
51.8
|
1.65
|
337
|
1600×3200 mm
|
|
5 mm
|
8.7 mm
|
0.05 mm
|
41.5
|
0.95
|
292
|
1600×3200 mm
|
|
6 mm
|
10.4 mm
|
0.06 mm
|
41.4
|
0.88
|
225
|
1600×4600 mm
|
|
8 mm
|
13.9 mm
|
0.07 mm
|
36.4
|
0.78
|
178
|
1600×4600 mm
|
|
10 mm
|
17.3 mm
|
0.07 mm
|
29
|
0.65
|
149
|
1600×4600 mm
|
|
12 mm
|
20.8 mm
|
0.08 mm
|
27.6
|
0.62
|
136
|
1600×7500 mm
|
|
15 mm
|
26 mm
|
0.08 mm
|
22.1
|
0.53
|
112
|
1600×7500 mm
|
|
20 mm
|
34.6 mm
|
0.08 mm
|
16.6
|
0.45
|
95
|
1600×9000 mm
|
铝蜂窝芯主要技术指标
|
项目
|
单位
|
实验结果
|
|
节点强度
|
Kg/cm2
|
1.5～1.7
|
|
板—芯90°剥离
|
? |
4.8～5.6
|
|
纵向弯曲强度
|
? |
8.6～11.6
|
|
横向弯曲强度
|
Kg/cm2
|
7.4～9.3
|
|
抗压强度
|
0.04/4
|
Kg/cm2
|
10～12
|
|
0.04/5
|
Kg/cm2
|
6～7.5
|
|
0.04/6
|
Kg/cm2
|
3～4.2
|
|
0.04/3
|
Kg/cm2
|
15～18
|
|
热膨胀系数
|
/℃
|
23×10-6
|
|
热传导率
|
W/M℃
|
1.7
|
- 燃烧性
|
不燃
|
铝蜂窝芯的性能
|
芯规格
|
密度kg/cm3
|
压缩稳定性
|
板剪切
|
|
强度Mpa
|
模量Mpa
|
L方向强度Mpa
|
L方向模量Mpa
|
W方向强度Mpa
|
W方向模量Mpa
|
|
1″
|
22.4
|
0.53
|
112
|
0.39
|
98
|
0.23
|
49
|
|
3/4″
|
28.5
|
0.77
|
168
|
0.67
|
112
|
0.39
|
56
|
|
3/8″
|
53.6
|
2.28
|
644
|
1.47
|
280
|
0.91
|
140
|
|
1/4″
|
81.8
|
4.34
|
1036
|
2.42
|
441
|
1.51
|
217
|
|
3/16″
|
117.4
|
5.25
|
1120
|
3.15
|
525
|
1.82
|
280
|
|
|